| Typical Data (Material and curing conditions @ 73°F (23°C) and 50% R.H.) |
| Shelf Life |
10.3 fl. os. cartridges - 15 Months |
| Storage Conditions |
Store at 40°-75°F. Condition material to 65°-75°F before using. |
| Colors |
White, colonial white, aluminum gray, limestone, black, dark bronze, capitol tan. |
| Application Temperature |
40° to 100°F. Sealant should be installed when joint is at mid-range of its anticipated movement. |
| Service Range |
-40° to 170°F (-40° to 75°C) |
| Curing Rate |
Tack-free time - 3 to 6 hours (TT-S-00230C)
Tack-free touch - 3 hours
Final cure - 7 to 10 days |
| Recovery |
>80% |
| Shore A Hardness (ASTM D-2240) |
21 day 25 ± 5 |
| Tensile Properties (ASTM D-412) |
21 Day |
Tensile Stress |
|
125 psi (.86 MPa) |
| |
Elongation at Break |
|
700% |
| |
Modulus of Elasticity |
25% |
20 psi (.13 MPa) |
| |
|
50% |
35 psi (.24 MPa)
|
| |
|
100% |
50 psi (.34 MPa) |
| Adhesion in Peel (TT-S-00230C) |
Substrate |
Peel Strength |
Adhesion Loss |
Aluminum
Glass
Concrete |
25 lb.
25 lb.
30 lb. |
0%
0%
0% |
| Weathering Resistance |
Excellent |
| Chemical Resistance |
Good resistance to water, diluted acids, and diluted alkalines. Not normally for fully immersed conditions. |